CO2 MIG Wire

  1. Home
  2. CO2 MIG Wire

MIGFAST €“ 1 (ER 70S-6)

A copper coated solid Steel wire for MIG/MAG welding of carbon steels. Used in the Automobile Industry, Construction and Mining Equipment, Railway Wagon and Coaches, Storage Tanks, Pressure Vessels, Steel Furniture, Pipes, LPG cylinders and Structural fabrications.

Approvals:
BHEL Trichy, NPCIL, M. N. Dastur & Co., Thermax, IBR (CIB Maharashtra)

CODING: ER 70S-6

TYPICAL ALL WELD ANALYSIS (%)

C: 0.06-0.15

Mn: 1.40 -1.85

Si: 0.80 -1.15

Mo: 0.15 max

Ni: 0.15 max

Cu: 0.50 max

S: 0.035 max

P: 0.025 max

Cr: 0.15 max

V: 0.03 max

MECHANICAL PROPERTIES

UTS Mpa: 500min.

Ys Mpa: 420min.

Elongation: 22% min

CVN Impact: 27J at -30°C

MIGFAST €“ 2 (ER 90S-D2)

A copper coated MIG wire for MIG/MAG welding of high tensile steels. Welding of SAILMA 450/450H1 steel used in CONCOR wagons is a typical application for this wire. Is used for welding of high tensile steels like IS 8500 Grades 540 B, 570 B, and 590B; IS 2002 Gr. III, IS 1875 Cl.

Approvals:
RDSO Class III ( Part-I)

CODING: ER 90S-D2

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07-0.12

Mn: 1.60 – 2.10

Si: 0.50 – 0.80

Mo: 0.40-0.60

Ni: 0.15 max

Cu: 0.50 max

S: 0.025 max

P: 0.025 max

MECHANICAL PROPERTIES

UTS Mpa: 620 min.

Ys Mpa: 540 min.

Elongation: 17% min.

CVN Impact: 27J at -30°C

MIGFAST €“ 3 (ER 70S-2)

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07 max

Mn: 0.90-1.40

Si: 0.40-0.70

Mo: 0.15 max

Ni: 0.15 max

Cu: 0.5 max

Ti: 0.05-0.15

Zr: 0.02-0.12

Al: 0.05-0.15

S: 0.03 max

P: 0.025 max

Ct: 0.15 max

MECHANICAL PROPERTIES

UTS Mpa: 480 min.

Ys Mpa: 400 min.

Elongation: 22% min.

CVN Impact: 27J at -30°C

CODING: ER 70S-2

Deoxidized copper coated mild steel wire. Structural, pressure vessels and boilers involving unalloyed and micro-alloyed structural steels. It meets HIC & SSCC test as per NACE specification.

MIGFAST €“ 5 (ER 90SG)

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07-0.12

Mn: 1.60 – 2.10

Si: 0.50-0.85

Mo: 0.40-0.65

Ni: 0.15 max

Cu: 0.50 max

S: 0.025 max

P: 0.025 max

MECHANICAL PROPERTIES

UTS Mpa: 625 min.

Ys Mpa: 550 min.

Elongation: 18% min.

CVN Impact: 27J at -46°C

CODING: ER 90SG

A copper-coated low-alloy steel gas-shielded welding wire. It is use for welding of high tensile strength steel, such as steel construction.

MIGFAST - 6(ER 80SG)

Coding: ER 80SG

TYPICAL ALL WELD ANALYSIS (%)

C: 0.10 max

Mn: 1.80 max

Si: 0.55 max

Mo: 0.50 max

Ni: 0.15 max

Cu: 0.50 max

S: 0.025 max

P: 0.025 max

MECHANICAL PROPERTIES

UTS Mpa: 600 min.

Ys Mpa: 470 min.

Elongation: 16% min.

CVN Impact: 40J at -20°C

MIGFAST-70S A1(ER 70S-A1)

CODING: ER 70S-A1

TYPICAL ALL WELD ANALYSIS (%)

C: 0.12 max

Mn: 1.30 max

Si: 0.30-0.70

Mo: 0.40-0.65

Cu: 0.35 max

S: 0.025 max

P: 0.025 max

MECHANICAL PROPERTIES

UTS Mpa: 515 min*

Ys Mpa: 400 min*

Elongation: 19% min*

CVN Impact: –

MIGFAST - 80S B2(ER 80S-B2)

CODING: ER 80S-B2

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07-0.12

Mn: 0.40-0.70

Si: 0.40-0.70

Mo: 0.40-0.65

Ni: 0.20 max

Cu: 0.35 max

S: 0.025 max

P: 0.025 max

Cr: 1.20-1.50

MECHANICAL PROPERTIES

UTS Mpa: 550 min*

Ys Mpa: 470 min*

Elongation: 19% min*

CVN Impact: –

MIGFAST - 80S B6(ER 80S-B6)

CODING: ER 80S-B6

TYPICAL ALL WELD ANALYSIS (%)

C: 0.10 max

Mn: 0.40-0.70

Si: 0.50 max

Mo: 0.45-0.65

Ni: 0.60 max

Cu: 0.35 max

S: 0.025 max

P: 0.025 max

Cr: 4.50-6.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min***

Ys Mpa: 470 min***

Elongation: 17% min***

CVN Impact: –

MIGFAST - 90S B3 (ER 90S-B3)

A copper coated MIG wire for MIG/MAG welding of high tensile steels. Welding of SAILMA 450/450H1 steel used in CONCOR wagons is a typical application for this wire. Is used for welding of high tensile steels like IS 8500 Grades 540 B, 570 B, and 590B; IS 2002 Gr. III, IS 1875 Cl.

Approvals:
RDSO Class III ( Part-I)

CODING: ER 90S-D2

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07-0.12

Mn: 1.60 – 2.10

Si: 0.50 – 0.80

Mo: 0.40-0.60

Ni: 0.15 max

Cu: 0.50 max

S: 0.025 max

P: 0.025 max

MECHANICAL PROPERTIES

UTS Mpa: 620 min.

Ys Mpa: 540 min.

Elongation: 17% min.

CVN Impact: 27J at -30°C

MIGFAST - 90S B9(ER 90S-B9)

CODING: ER 90S-B9

TYPICAL ALL WELD ANALYSIS (%)

C: 0.07-0.13

Mn: 1.20 max

Si: 0.15-0.50

Mo: 0.85-1.20

Ni: 0.80 max

Cu: 0.20 max

Al: 0.04 max

S: 0.01 max

P: 0.01 max

Cr: 8.00-10.50

V: 0.15-0.30

MECHANICAL PROPERTIES

UTS Mpa: 620 min****

Ys Mpa: 410 min****

Elongation: 16% min****

CVN Impact: –

MIGFAST 308(ER 308)

CODING: ER 308

TYPICAL ALL WELD ANALYSIS (%)

C: 0.08 max

Mn: 1.00-2.50

Si: 0.30-0.65

Ni: 9.00-11.00

Cr: 19.50-22.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 35% min

CVN Impact: –

MIGFAST 308L(ER 308L)

CODING: ER 308L

TYPICAL ALL WELD ANALYSIS (%)

C: 0.03 max

Mn: 1.00-2.50

Si: 0.30-0.65

Ni: 9.00-11.00

Cr: 19.50-22.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 35% min

CVN Impact: –

MIGFAST 347(ER 347)

CODING: ER 347

TYPICAL ALL WELD ANALYSIS (%)

C: 0.08 max

Mn: 1.00-2.50

Si: 0.30-0.65

Ni: 9.00-11.00

Cr: 19.00-21.50

Nb:  1.0 max

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 30% min

CVN Impact: –

MIGFAST 316(ER 316)

CODING: ER 316

TYPICAL ALL WELD ANALYSIS (%)

C: 0.08 max

Mn: 1.00-2.50

Si: 0.30-0.65

So: 2.00-3.00

Ni: 11.00-14.00

Cr: 18.00-20.00

MECHANICAL PROPERTIES

UTS Mpa: 520 min

Elongation: 30% min

CVN Impact: –

MIGFAST 316 L (ER 316L)

CODING: ER 316L

TYPICAL ALL WELD ANALYSIS (%)

C: 0.03 max

Mn: 1.00-2.50

Si: 0.30-0.65

Mo: 2.00-3.00

Ni: 11.00-14.00

Cr: 18.00-20.00

MECHANICAL PROPERTIES

UTS Mpa: 490 min

Elongation: 30% min

CVN Impact: –

MIGFAST 309 (ER 309)

CODING: ER 309

TYPICAL ALL WELD ANALYSIS (%)

C: 0.12 max

Mn: 1.00-2.50

Si: 0.30-0.65

So: 2.00-3.00

Ni: 12.00-14.00

Cr: 23.00-25.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 30% min

CVN Impact: –

MIGFAST 309L (ER 309L)

CODING: ER 309L

TYPICAL ALL WELD ANALYSIS (%)

C: 0.03 max

Mn: 1.00-2.50

Si: 0.30-0.65

So: 2.00-3.00

Ni: 12.00-14.00

Cr: 23.00-25.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 30% min

CVN Impact: –

MIGFAST 309 Mo (ER 309Mo)

CODING: ER 309Mo

TYPICAL ALL WELD ANALYSIS (%)

C: 0.12 max

Mn: 1.00-2.50

Si: 0.30-0.65

Mo: 2.00-3.00

So: 2.00-3.00

Ni: 12.00-14.00

Cr: 23.00-25.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 30% min

CVN Impact: –

MIGFAST 310 (ER 310)

CODING: ER 310

TYPICAL ALL WELD ANALYSIS (%)

C: 0.08-0.15

Mn: 1.00-2.50

Si: 0.30-0.65

Ni: 20.00-22.50

Cr: 25.00-28.00

MECHANICAL PROPERTIES

UTS Mpa: 550 min

Elongation: 30% min

CVN Impact: –

MIGFAST 312 (ER 312)

CODING: ER 312

TYPICAL ALL WELD ANALYSIS (%)

C: 0.15 max

Mn: 1.00-2.50

Si: 0.30-0.65

Ni: 8.00-10.50

Cr: 28.00-32.00

MECHANICAL PROPERTIES

UTS Mpa: 660 min

Elongation: 22% min

CVN Impact: –

MIGFAST 410 (ER 410)

CODING: ER 410

TYPICAL ALL WELD ANALYSIS (%)

C: 0.12 max

Mn: 0.60 max

Si: 00.50 max

Cr: 11.50-13.50

MECHANICAL PROPERTIES

UTS Mpa: 520 min

Elongation: 20% min

CVN Impact: –

MIGFAST 430 ( ER 430)

CODING: ER 430

TYPICAL ALL WELD ANALYSIS (%)

C: 0.10 max

Mn: 0.60 max

Si: 00.50 max

Cr: 15.50-17.00

MECHANICAL PROPERTIES

UTS Mpa: 450 min

Elongation: 20% min

CVN Impact: –

MIGFAST €“ 625 (ER NiCrMo3)

CODING: ER NiCrMo3

TYPICAL ALL WELD ANALYSIS (%)

C: 0.10 max

Mn: 0.50 max

Si: 0.50 max

Mo: 8.0-10.0

Ni: 58% min

Cu: 0.50 max

Ti: 0.40 max

Fe: 5.00 max

Al: 0.40 max

S: 0.015 max

P: 0.02 max

Cr: 20.0-23.0

Nb+Ta: 3.15-4.15

MECHANICAL PROPERTIES

UTS Mpa: 760 Typical

Elongation: –

CVN Impact: –